张希/刁东风等在Advanced Materials Interfaces发表封面论文阅读次数 [1642] 发布时间 :2019-04-27 09:44:28

我所论文：Edge-State-Enhanced Ultrahigh Photoresponsivity of Graphene Nanosheet-Embedded Carbon Film/Silicon Heterojunction，发表于JCR2区国际期刊Advanced Materials Interfaces，并选为封面论文。

Edge-State-Enhanced Ultrahigh Photoresponsivity of Graphene Nanosheet-Embedded Carbon Film/Silicon Heterojunction

Adv. Mater. Interfaces 2019, 1802062

Xi Zhang, Zezhou Lin, Da Peng, Lei Ye, Jianfeng Zang, and Dongfeng Diao*

Lacking of electron trapping centers hinders the development of plane graphene for sensitive photodetection. An

ultrasensitive graphene nanosheetembedded carbon (GNEC) film/silicon photodetector is proposed by introducing high-density edges of standing structured graphene nanosheets (GNs). The GNEC film is prepared to contain a large amount of vertically grown GNs. The high-density edges are able to trap itinerate electrons to tune the Fermi level of GNs in the growing process and to capture the photoexcited electrons to reduce the electron–hole recombination rate in the photovoltaic process. An ultrahigh responsivity of 61.52 A W−1 of GNEC film/Si photodetector is achieved, ≈20 times of graphene/Si photovoltaic detectors. A high specific detectivity of 3.05 × 1014 Jones (approximately two orders improved) is obtained at bias-free mode. This work sheds light on the edge engineering of 2D materials in the third dimension in order for enhancing photoelectronic performance.