张希/刁东风在Physica Status Solidi-Rapid Research Letters发表论文阅读次数 [1536] 发布时间 :2019-02-18 15:52:38

我所论文：Edge Effect on the Photodetection Ability of the Graphene Nanocrystallites Embedded Carbon Film Coated on p-Silicon，发表于JCR2区期刊Physica Status Solidi-Rapid Research Letters。

Edge Effect on the Photodetection Ability of the Graphene Nanocrystallites Embedded Carbon Film Coated on p-Silicon

Phys. Status Solidi RRL 2019, 1800511（PDF-File）

Xi Zhang, Da Peng, Zezhou Lin, Wencong Chen, and Dongfeng Diao*

A sensitive photodetector of graphene nanocrystallites embedded carbon (GNEC) film coated on p-silicon has been proposed. Different from the conventional growth mode of graphene, GNEC film contains a large amount of vertically grown graphene nanocrystallites (GNs). Edges of GNs act as electron trapping centers, increasing the ability to capture electrons. Different types of films are prepared under various deposition biases (20, 40, 60, and 80 V), which have different density of edges (Nedge). Edge entrapment improves the photocurrent responsivity of 40 V film (high Nedge) to 0.401 A W
1, compared with 0.126 AW
1 of 20 V film (amorphous, no Nedge) and 0.194 AW
1 of 80 V film (low Nedge). A high specific detectivity of 1.341012 cm Hz1/2W
1 is exhibited at zero bias. GNs maintain a charge transport channel, which makes it have a fast response time τrise¼260 ns.